LS 80/150
- Grammage 150±5 g/m2
- Pressing time 300-480 s
- Pressing temperature 130-138 °C
- Resin content 45...50%
- Volatile 6.5...7.5%
- Type roll
- Size 1500 m
- Content of the water-soluble fractions no less 60%
- Degree of the spreadability of the resin in the paper 1,5...2.0 %
- Purpose Postformed decorative laminates
The phenolic paper (paper impregnated with phenol-formaldehyde resin, modified melamine) is a half-finished product for the production of decorative laminates (dBHL), prepared by the method of CPL, and is used as the inner layers for the postformed decorative laminates.
LS 80/150 TU 5459-002-69073969-2015 - Laminate Samara - phenolic paper-based kraft paper weighing 80 g / m2 for the inner layers of the CPL- Decorative Laminates
- Grammage 150±5 g/m2
- Pressing time 300-480 s
- Pressing temperature 130-138 °C
- Resin content 45...50%
- Volatile 6.5...7.5%
- Type roll
- Size 1500 m
- Content of the water-soluble fractions no less 60%
- Degree of the spreadability of the resin in the paper 1,5...2.0 %
- Purpose Postformed decorative laminates
Recommend products
The paper impregnated with phenolic resin for Decorative Laminates
LS 80/150
LS 80/150
Grammage
150±5 g/m2
Pressing time
300-480 s
Pressing temperature
130-138 °C
The paper impregnated with phenolic resin for Decorative Laminates
LS 155/300
LS 155/300
Grammage
300±5 g/m2
Pressing time
300-480 s
Pressing temperature
160-190 °C
The paper impregnated with phenolic resin for Decorative Laminates
PAFF 155/230
PAFF 155/230
Grammage
230±5 g/m2
Pressing temperature
160-190 °C
The paper impregnated with phenolic resin for Decorative Laminates
LS 155/230 ST
LS 155/230 ST
Grammage
230±5 g/m2
Pressing time
60-80 min.
Pressing temperature
130-160 °C
The paper impregnated with phenolic resin for Decorative Laminates
LS 155/230 PF
LS 155/230 PF
Grammage
230±5 g/m2
Pressing time
60-80 min.
Pressing temperature
130-160 °C
The paper impregnated with phenolic resin for Decorative Laminates
LS 155/230 Black
LS 155/230 Black
Grammage
230±5 g/m2
Pressing time
60-80 min.
Pressing temperature
130-160 °C